Chuck Metals stands out as a trusted manufacturer and supplier based in Singapore, Pulau Ujong, known for its top-notch High Speed Steel (HSS) M42 Bars. These bars are celebrated for their remarkable hardness, wear resistance, and their ability to maintain cutting performance even at high temperatures. Crafted to meet rigorous quality standards, they’re perfect for precision tooling applications across demanding industries. With a high cobalt content and outstanding toughness, Chuck Metals guarantees that each M42 bar is built for durability, precise dimensions, and a superb surface finish, catering to sectors like aerospace, automotive, and heavy engineering with reliable, high-performance solutions.
High Speed Steel M42 Bars are primarily made up of carbon, tungsten, molybdenum, vanadium, chromium, and about 8% cobalt, which greatly enhances their red hardness and cutting efficiency. This alloy boasts exceptional abrasion resistance, hot hardness, and toughness, with tensile strength usually exceeding 3000 MPa and hardness levels ranging from 66 to 70 HRC after heat treatment. The blend of these alloying elements ensures outstanding performance in high-speed and high-temperature cutting scenarios.
| ASTM A600 | C | Mn | P | S | Si | Cr | V | Mo | W | Co | ||||||||
| M42 | 1.05 | 1.15 | 0.15 | 0.40 | 0.03 | 0.03 | 0.15 | 0.65 | 3.50 | 4.25 | 0.95 | 1.35 | 9.00 | 10.00 | 1.15 | 1.85 | 7.75 | 8.75 |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | W | Co | ||||||||
| 1.3247/HS2-9-1-8 | 1.05 | 1.15 | … | … | … | … | … | 0.70 | 3.50 | 4.50 | 0.90 | 1.30 | 9.00 | 10.00 | 1.20 | 1.90 | 7.50 | 8.50 |
| JIS G4403 | C | Mn | P | S | Si | Cr | V | Mo | W | Co | ||||||||
| SKH59 | 1.05 | 1.15 | … | 0.40 | 0.03 | 0.03 | … | 0.70 | 3.50 | 4.50 | 0.90 | 1.30 | 9.00 | 10.00 | 1.20 | 1.90 | 7.50 | 8.50 |
| Mechanical Properties | Metric | Imperial |
| Hardness, Rockwell C (oil quenched from 1204°C, 5 minutes) | 64.3 | 64.3 |
| Hardness, Rockwell C (oil quenched from 1177°C, 5 minutes) | 65.5 | 65.5 |
| Hardness, Rockwell C(oil quenched from 1163°C) | 65.8 | 65.8 |
| Izod impact unnotched (oil quenched at 1191°C; 510°C temper temperature) | 13.6 J | 10.0 ft- lb |
| Izod impact unnotched (oil quenched at 1191°C; 622°C temper temperature) | 24.4 J | 24.4 J |
| Machinability (1% carbon steel) | 35.0 – 40.0% | 35.0 – 40.0% |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elastic modulus | 190-210 GPa | 27557-30457 ksi |
| Country | USA | German | Japan |
| Standard | ASTM A600 | DIN EN ISO 4957 | JIS G4403 |
| Grades | M42 | 1.3247/HS2-9-1-8 | SKH59 |
Yes, High-Speed Steel M42 can be welded, but it requires specialized techniques like preheating, post-weld heat treatment, and using appropriate filler materials to avoid cracking and maintain its properties.
Yes, High Speed Steel M42 bars are recyclable. They can be melted and reused in manufacturing, reducing waste and conserving resources, making them an environmentally friendly material choice.
These High Speed Steel M42 Bars are extensively utilized in the production of high-performance cutting tools like drills, taps, milling cutters, and reamers that function at elevated speeds and temperatures. They are crucial for machining tough materials such as stainless steels, titanium alloys, and heat-resistant superalloys. Commonly found in aerospace, automotive, and die-making industries, these bars offer extended tool life, precision, and efficiency. Their ability to retain hardness and sharpness under extreme conditions makes them the go-to choice for high-volume production and critical machining tasks.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Chuck Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Singapore, Singapore